Corrosion behavior of Sn-9Zn-xBi lead-free solder alloys in NaCl 3% solution

AdnaneAhmido, Souad El Hajjaji, Benaceur Ouaki,A.Sabbar, Saloua Sebbahi


Corrosion behavior of Sn–9Zn-xBi alloys (x=0; 0.5 and 3 wt%) were studied in NaCl 3% solution using open circuit potential, polarization curves, weight loss measurements and surface analysis. The obtained results revealed the corrosion resistance depends on the percentage of bismuth. The Sn-9Zn-3Bi has the lowest values of corrosion current density. The corrosion potential shift toward more negative values with more bismuth addition. XRD analysis of the corrosion products formed after 168 hours of immersion in NaCl 3% solution indicated the zinc dissolution.


Индексировано в

  • КАСС
  • Google Scholar
  • Открыть J-ворота
  • Национальная инфраструктура знаний Китая (CNKI)
  • CiteFactor
  • Космос ЕСЛИ
  • Библиотека электронных журналов
  • Каталог индексирования исследовательских журналов (DRJI)
  • Секретные лаборатории поисковых систем
  • ICMJE

Посмотреть больше

Журнал ISSN

Индекс Хирша журнала

Flyer

Журналы открытого доступа